Product description 产品描述
This kind of products is applicable for 35KV cross-linkable semi-conductive shielding between conductors of extrusion insulation power cables and insulation layers. It is manufactured with importing raw materials by Swiss BUSS KKG-14/18 extrusion equipment through compounding process. The surface of the cables is smooth and deeply loved by famous cable manufacturers both domestic and abroad.
本产品适用于35KV及以下挤包绝缘电力电缆导体与绝缘层交联型半导电屏蔽，采用进口原辅助材料经先进的瑞士BUSS设备混炼加工而成，制成电缆表面光滑圆整，本产品深受海内外著名电缆跨国公司的青睐。
 
Processing Indicator 加工工艺
Recommend to process with the PE extruder. 建议使用聚乙烯专用挤出机进行加工。

Model 牌号	Machine Barrel Temperature 机筒温度	Molding Temperature 机头温度
DWPJ-5035/DWPB-8035	70-115℃	110-117℃

 
Physical and Electrical Properties 物理和电气性能

Item 试验项目	Unit 单位	Technical requirements 技术要求
		DWPJ-5035	DWPB-8035
Relative Density 相对密度	g/cm3	≤1.14	≤1.17
Tensile Strength 拉伸强度	MPa	≥15	≥12
Elongation at Break 断裂伸长率	%	≥230	≥260
20℃Volume Resisitivity 20℃体积电阻率	Ω·cm	≤50	≤100
Volume Resisitivity 体积电阻率90℃	Ω·cm	≤1000	≤1500
90℃Volume Resisitivity after air aging(100℃×168h) 100℃168小时空气热老化后 90℃时体积电阻率	Ω·cm	≤800	≤1000
Air aging test 空气热老化试验	/	(135±2℃)×168h
Tensile Strength Variation After Aging 拉伸强度变化率	%	±25	±25
Elongation Variation After Aging 断裂伸长变化率	%	±25	±25
Hot Set Test 热延伸		200℃×0.2MPa×15min
Hot Elongation 负荷下伸长率(Hot)	%	≤100	≤100
Permanent Deformation after Cooling 冷却后永久变形(Set)	%	≤15	≤15
Peel Strength 剥离强度20℃	N/cm	----	10-35